SA335 P12 je čelična cijev od legure hrom-molibdena prema ASTM standardu, hemijskog sastava 1Cr-0,5Mo (C<0.15%, Cr0.8-1.25%, Mo0.44-0.65%). Its high-temperature strength is significantly improved through the solid solution strengthening effect of aluminum. Compared to ordinary 20G boiler tubes, its creep strength at 540°C is increased by approximately 40%, and the allowable stress can reach 78MPa (ASME standard). This material must simultaneously meet the triple standards of ASTM A335 (materials), A213 (cold drawing), and A370 (mechanical testing), and must undergo 100% eddy current testing and hydraulic testing (test pressure >60MPa) prije izlaska iz fabrike.

Specifikacija

P12 čelične cijevi su obično dostupne u veličinama u rasponu od 25-762 mm u promjeru i 3-50 mm u debljini zida.

Ključne tehnologije u proizvodnom procesu

Proizvodnja visoko-kvalitetnih čeličnih cijevi SA335 P12 zahtijeva kontrolu nad tri osnovna aspekta:

1. Proces topljenja koristi trostruki proces EAFLFVD, kontrolišući sadržaj sumpora i fosfora na manje od ili jednako 0,015% i sadržaj vodonika na manje od ili jednako 2ppm;

2. Vruće valjanje koristi dvostepeni kontrolirani proces valjanja, sa završnom temperaturom valjanja kontroliranom na 880±20 stepeni kako bi se osigurala potpuna rekristalizacija austenita;

3. Termička obrada mora biti u skladu sa režimom normalizacije (900-930 stepeni) i temperiranja (680-730 stepeni), što rezultira ujednačenom mikrostrukturom kaljenog bainita.

Prijave

U superkritičnim kotlovskim jedinicama, P12 čelične cijevi se uglavnom koriste u:
Nisko{0}}pregrijači (temperatura zida manja ili jednaka 450 stepeni)
Zaglavlja ekonomajzera
Sistemi potpore glavnih parnih cijevi

SA335 P12 tvornica visokotemperaturnih legura cijevi